HS Code |
157832 |
| Product Name | Chlorosulfonated Polyethylene Anticorrosive Paint J52-32 |
| Type | Single-component |
| Main Component | Chlorosulfonated polyethylene resin |
| Appearance | Flat finish, variety of colors |
| Theoretical Coverage | 8-10 m²/kg (at 30 microns dry film thickness) |
| Drying Time Surface | ≤ 1 hour (at 25°C) |
| Complete Cure Time | ≤ 24 hours (at 25°C) |
| Recommended Dry Film Thickness | 30-40 microns per coat |
| Adhesion | ≤ 1 grade (GB/T 1720 standard) |
| Hardness | ≥ 0.25 (pencil hardness, GB/T 6739 standard) |
| Flexibility | ≤ 1 mm (GB/T 1731 standard) |
| Water Resistance | ≥ 72 hours (no abnormality) |
| Salt Spray Resistance | ≥ 200 hours (no blistering or rust) |
| Application Methods | Brushing, spraying, rolling |
| Storage Life | 12 months (in cool, dry conditions, unopened) |
As an accredited Chlorosulfonated Polyethylene Anticorrosive Paint J52-32 factory, we enforce strict quality protocols—every batch undergoes rigorous testing to ensure consistent efficacy and safety standards.
| Packing | Chlorosulfonated Polyethylene Anticorrosive Paint J52-32 is packaged in 20 kg metal drums, securely sealed to prevent leakage. |
| Container Loading (20′ FCL) | Container Loading (20′ FCL): Chlorosulfonated Polyethylene Anticorrosive Paint J52-32—holds 16-20 tons, packed in 200kg steel drums. |
| Shipping | Chlorosulfonated Polyethylene Anticorrosive Paint J52-32 must be shipped in tightly sealed, labeled containers, protected from direct sunlight, moisture, and extreme temperatures. Handle with care to prevent leakage. Transport in accordance with local chemical safety regulations, ensuring the shipment remains upright and secure to avoid spills, damage, or contamination. |
| Storage | Chlorosulfonated Polyethylene Anticorrosive Paint J52-32 should be stored in tightly sealed containers, in a cool, dry, and well-ventilated area, away from direct sunlight, heat sources, and open flames. Avoid exposure to moisture and incompatible substances. Keep out of reach of children and unauthorized personnel. Ensure proper labeling, and handle with care to prevent spillage or leakage. |
| Shelf Life | The shelf life of Chlorosulfonated Polyethylene Anticorrosive Paint J52-32 is typically 12 months when stored in a cool, dry place. |
|
Viscosity grade: Chlorosulfonated Polyethylene Anticorrosive Paint J52-32 with high viscosity is used in marine structural steel protection, where it provides enhanced film thickness and prolonged corrosion resistance. Purity 99%: Chlorosulfonated Polyethylene Anticorrosive Paint J52-32 with 99% purity is used in petrochemical plant pipeline coatings, where it ensures high chemical stability and minimal contamination risk. Molecular weight 120,000: Chlorosulfonated Polyethylene Anticorrosive Paint J52-32 with a molecular weight of 120,000 is used in bridge surface treatments, where it improves mechanical durability against abrasion and weathering. Stability temperature 120°C: Chlorosulfonated Polyethylene Anticorrosive Paint J52-32 with stability temperature of 120°C is used in heat exchanger exterior coatings, where it maintains anti-corrosive performance under thermal cycling. Particle size ≤20μm: Chlorosulfonated Polyethylene Anticorrosive Paint J52-32 with particle size ≤20μm is used in offshore platform surface finishing, where it ensures smooth application and uniform coating coverage. Solid content 60%: Chlorosulfonated Polyethylene Anticorrosive Paint J52-32 with solid content of 60% is used in storage tank external painting, where it provides a dense protective layer with superior weathering endurance. Drying time ≤2 hours: Chlorosulfonated Polyethylene Anticorrosive Paint J52-32 with a drying time of ≤2 hours is used in industrial equipment maintenance, where it allows rapid turnaround and efficient schedule adherence. Adhesion strength ≥5MPa: Chlorosulfonated Polyethylene Anticorrosive Paint J52-32 with adhesion strength ≥5MPa is used on machinery chassis, where it delivers strong substrate bonding for long-term integrity. VOC content ≤50g/L: Chlorosulfonated Polyethylene Anticorrosive Paint J52-32 with VOC content ≤50g/L is used in confined space applications, where it reduces environmental impact and enhances safety compliance. Flexibility at -30°C: Chlorosulfonated Polyethylene Anticorrosive Paint J52-32 with flexibility at -30°C is used in outdoor infrastructure in cold climates, where it resists cracking and maintains barrier performance. |
Competitive Chlorosulfonated Polyethylene Anticorrosive Paint J52-32 prices that fit your budget—flexible terms and customized quotes for every order.
For samples, pricing, or more information, please contact us at +8615651039172 or mail to sales9@bouling-chem.com.
We will respond to you as soon as possible.
Tel: +8615651039172
Email: sales9@bouling-chem.com
Flexible payment, competitive price, premium service - Inquire now!