HS Code |
655424 |
| Productname | Epoxy Micaceous Iron Oxide Primer H06-12 |
| Type | Epoxy Primer |
| Maincomponents | Epoxy resin and micaceous iron oxide |
| Color | Gray |
| Finish | Semi-matte |
| Mixingratio | Base : Hardener = 4:1 by volume |
| Dryfilmthickness | 60-80 microns per coat |
| Theoreticalcoverage | 8-10 m²/L at 60 microns DFT |
| Dryingtimetouch | 2 hours at 25°C |
| Recoatinginterval | Minimum 16 hours at 25°C |
| Surfacepreparation | Abrasive blasting to Sa2.5 |
| Thinner | Epoxy thinner |
| Applicationmethod | Brush, roller, or spray |
| Purpose | Corrosion resistance and adhesion on steel substrates |
As an accredited Epoxy Micaceous Iron Oxide Primer H06-12 factory, we enforce strict quality protocols—every batch undergoes rigorous testing to ensure consistent efficacy and safety standards.
| Packing | Epoxy Micaceous Iron Oxide Primer H06-12 is typically packaged in a 20-liter metal drum, featuring a secure, corrosion-resistant lid. |
| Container Loading (20′ FCL) | Epoxy Micaceous Iron Oxide Primer H06-12 is loaded into a 20′ FCL, securely packed in drums or pails for export. |
| Shipping | Epoxy Micaceous Iron Oxide Primer H06-12 is shipped in sealed, corrosion-resistant containers to prevent moisture ingress. All packaging complies with hazardous material regulations, ensuring safe handling and transport. Proper labeling and documentation are provided, with shipping carried out by certified carriers to guarantee product integrity and environmental safety during transit. |
| Storage | Epoxy Micaceous Iron Oxide Primer H06-12 should be stored in a cool, dry, and well-ventilated area, away from direct sunlight, heat sources, and open flames. Keep containers tightly sealed to prevent contamination and evaporation. Avoid freezing temperatures and excessive humidity. Store away from incompatible materials such as strong acids and oxidizers. Always follow local safety regulations and manufacturer's guidelines for storage. |
| Shelf Life | Epoxy Micaceous Iron Oxide Primer H06-12 has a shelf life of 12 months in unopened containers, stored under cool, dry conditions. |
|
Purity 99%: Epoxy Micaceous Iron Oxide Primer H06-12 with purity 99% is used in offshore platform steel structures, where it ensures excellent anticorrosion performance and enhanced surface durability. Viscosity grade 80 KU: Epoxy Micaceous Iron Oxide Primer H06-12 of viscosity grade 80 KU is used in ship hull maintenance, where it provides superior flow and uniform coverage, minimizing application defects. Micaceous iron oxide content 35%: Epoxy Micaceous Iron Oxide Primer H06-12 with micaceous iron oxide content 35% is used in petrochemical plant piping, where it offers outstanding resistance to chemical permeation and prolongs service life. Pot life 6 hours: Epoxy Micaceous Iron Oxide Primer H06-12 with a pot life of 6 hours is used in large-scale bridge coating projects, where it allows sufficient working time for efficient application and seamless film formation. Adhesion strength 8 MPa: Epoxy Micaceous Iron Oxide Primer H06-12 with adhesion strength of 8 MPa is used in water treatment facility tanks, where it promotes strong substrate bonding and prevents paint delamination. Stability temperature 120°C: Epoxy Micaceous Iron Oxide Primer H06-12 with stability temperature of 120°C is used in power plant exhaust stacks, where it maintains protective properties under high-thermal cycling conditions. Dry film thickness 60 μm: Epoxy Micaceous Iron Oxide Primer H06-12 with dry film thickness 60 μm is used in industrial machinery coating, where it achieves optimal barrier protection against moisture and aggressive agents. Solids content 65%: Epoxy Micaceous Iron Oxide Primer H06-12 with solids content 65% is used in marine deck surfaces, where it delivers high-build characteristics and long-term wear resistance. VOC content below 200 g/L: Epoxy Micaceous Iron Oxide Primer H06-12 with VOC content below 200 g/L is used in enclosed environment painting, where it meets regulatory compliance and reduces potential health hazards. Particle size < 40 μm: Epoxy Micaceous Iron Oxide Primer H06-12 with particle size less than 40 μm is used in architectural steel facade protection, where it ensures smooth texture and uniform color consistency. |
Competitive Epoxy Micaceous Iron Oxide Primer H06-12 prices that fit your budget—flexible terms and customized quotes for every order.
For samples, pricing, or more information, please contact us at +8615651039172 or mail to sales9@bouling-chem.com.
We will respond to you as soon as possible.
Tel: +8615651039172
Email: sales9@bouling-chem.com
Flexible payment, competitive price, premium service - Inquire now!